Effect of Er: YAG laser irradiation with additional low energy on resin-dentin bonding and morphology of bonded interface

Objectives: To examine the micro tensile bond strength (μTBS) and the resin-dentin interface on a laser-irradiated dentin surface using two different irradiation methods, with or without additional low-energy irradiation. Methods: The flat bovine dentin surface was divided into three groups: i). control group (C group, no irradiation), ii) 80 mJ/pulse Er: YAG laser group (80 group), iii) 80 + 30 mJ/pulse Er: YAG laser group (80 + 30 group, with an additional 30 mJ/pulse). After the roughness of the dentin surface was recorded, Clearfil SE Bond 2 or Clearfil Universal Bond Quick (Kuraray Noritake Dental Inc., Tokyo, Japan) was applied. After the μTBS testing, the failure mode was observed. The bonded interface was assessed using Rhodamine-dye incorporated adhesives and observed by optical coherence tomography. Results: The dentin surface showed opened dentinal tubules without a smear layer after irradiation. For both adhesives, the μTBS was significantly higher in 80 + 30 group than in the 80 group (p < 0.05). In the 80 group, the thickness of the adhesive layer was not uniform, and the dentin surface was occasionally in direct contact with the composite resin. The failure mode images showed that most of the fractures in the 80 group were at the sub-surface of irradiated dentin. The adhesive layers of the 80 + 30 groups were homogeneous. Conclusions: The dentin surface was rough and irregular by 80 mJ irradiation, which might result in an inadequate resin-dentin interface and the weak μTBS. The bonded integrity was mitigated by additional irradiation.